KSM-S6189GL05 is photoimageable solder mask. It has good screen printing
adaptability , excellent adhesion , high resistance to chemicals and heat. It has
extensive operating conditions . This liquid photoimageable solder mask possesses
easy operation and is wildly accepted.Properties of ink :Items | Features | Notes |
Color | Green | |
Fineness | ≤8µm | 0 ~25µm Fineness gauge |
Mix ratio | Base/Hardener=3:1 | Weight ratio |
Solid content after mixing | 75±3% | |
Viscosity after mixing (25ºC) | 200±30 dPa.s | VT-04F |
Density after mixing (25ºC) | 1.20 ~1.30 g/ml | |
Pot life after mixing | 24 hour | Store below 25ºC in dark |
Pre-baking limit | 75ºC , 60 min | |
Exposure energy | 400 ~600 mJ/cm2 | The effective value through the polyester film |
Package | Base :750g , Hardener :250 g | Conventional Packaging |
Shelf life | 6 months since the date of manufacture | Store below 25ºC in dark |
Properties of the film (after post cured)Items | Features | Notes |
Pencil hardness | ≥6H | Pencil harder,JIS K5400 8.4 |
Adhesion | 100/100 | Laceration experiment,JIS K5400 8.5 |
Solvent resistance | Good | 25ºC,C2H5OH ,20min |
Acid resistance | Good | 25ºC,10vol%H2SO4 ,20min |
Alkali resistance | Good | 25ºC,10wt%NaOH ,20min |
Boiling water resistance | Good | 100ºC, 30min |
Insulation resistance | ≥1.0×1012Ω | IPC-SM-840C 3.8.2 |
CTI | ≥600 | IEC 60112:2003 |
Resistance to molten solder | 288ºC×10 seconds×3 times OK | JIS C6481 5.5 |
Resistance to flame | UL94V-0 | Certified number:UL-E189612 |
Chemical-plating nickel/aurum | OK | Ni:5μm; Au:0.05μm |
Attention :
1. The base and hardener should be mixed according to the ratio and stirred thoroughly before using.2. We will offer you special diluent if the ink need dilute.
3. The values above are based on experiments in our lab. Experiments need to be
carried out in order to get proper using condition.Liquid photoimageable solder mask directions of use
1.Working procedureProcedure | Content |
(1) Mixing | Mixing about 30g main agent with hardener and stirring thoroughly,then mixing the mixture above with the remanent main agent and stirring 5 ~10 minutes. The viscosity of ink is adjusted to 120±20 ps if printed by hand. And it is adjusted to 160 ± 20 ps if printed by machine. The viscosity of ink mixed above is measured at 25 ºC .Please use the special diluent of our company if the viscosity of ink needs to adjust. |
(2) Remain time | 10 ~15 minutes after stirring uniformly |
(3) Screen mesh | Ordinary boards:43T ; Chemical-plating Aurum or Tin boards:36T |
(4) Pre-baking | 1. Single side printing separately First side :72 ~76ºC ,20 ~25min Second side : 72 ~76ºC , 30 ~35min 2. Double sides printing simultaneously : 72 ~76ºC , 40 ~60min |
(5) Exposure | 400~600mJ/cm2(the effective value through the polyester film), 10~12 step |
(6) Developing | Developing solution :0.8 ~1.2wt%Na2CO3 or K2CO3 aqueous solution Developing solution temperature :28 ~32ºC Spray pressure:2.5~3.0kg/cm2 Developing time:60~90 seconds |
(7) Post cure | Spray Tin board:150ºC×60~120 min;Chemical-plating Aurum or Tin board:150ºC×50~60 min; boards filled with ink in the hole should be post-baked in subsection:75ºC×60~120 min+100ºC×30 min+150ºC×60 min |
2. Caution 1. Requirements of working place :the temperature should be 20~24ºC and humidity is 55~65% in the room for printing and exposure without dust. Please work in the place without UV ray , or it will cause photo polymerization if the ink is used in the irradiation of white ray or sunlight. |
2. Mixing the main agent with hardener and stirring thoroughly and using only in room temperature. |
3. Appropriate film thickness is from 18 to 22μm. Thinner film will reduce the resistance to heat , chemicals and plating. Thicker film will cause excess under-cut and reduce the degree of dryness because the irradiation can not cure the botton layer of the ink. |
4. The screen boards can not be pasted with adhesion tape directly or else the remanent mucus will cause hollow pot on board. |
5.The ink can not be printed into the accessory hole. Developing time should be increased if ink gets into the accessory hole or there will be uncleaned. |
6. The condition and allowed range of pre-baking vary with the oven type and different number of boards in the oven. Experiments need to be carried out to get proper condition. |
7. Exposure energy varies with the board material and ink thinkness. Experiments should be carried out to determine the minimum width , surface gloss and the sensitization of the botton surface and then set proper condition. |
8.Inadequate developing temperature and time may cause unclean developing and over of them can cause excess under-cut and the feature of ink will be influenced because of the attack of ink surface. Please control the concentration of developing solution , temperature , pressure and developing time strictly. Experiments need to be carried out to get proper condition. |
9. The ink is easy to remove when the temperature and time of post-baking is deficient. It will reduce the resistance to plating aurum and molten solder when the post-baking time is over 2.5 hours. Experiments need to be carried out to set proper conditions of spraying tin and plating aurum. |
10. Experiment whether the ink can afford attack of the process of wave crest solder when the flux is rosin. |
11. Taphole boards are baked in subsection : 75ºC×60~120 min+100ºC×30 min+150×60 min. |
12. Please set proper post-baking tine of solder resist to suit for printing marking ink.Deficient or over hardening can reduce the feature of ink. |
13. Condition of chemical-plating aurum : A. use 36T screen for printing. B. The sensitization of exposure energy is 10 to 12 step. C. Under-cut is controlled below 1 mil after developing or the film will easily be attacked by the liquid medicine in the process of chemical-plating aurum. D. The film need to cure through the UV bump again if the exposure is not enough . E. Chemical-plate aurum or tin first and then print marking ink. or excess hardening will reduce the resistance to chemical properties. |
Company profile
JIANGSU KUANGSHUN PHOTOSENSITIVITY NEW-MATERIAL STOCK CO., LTD.. committed to development and production of high-tech and high grade new photosensitive materials, mainly engaged in R & D, production and sales of PCB ink. The company has a high performance of independent R & D capability, is the leading domestic PCB ink manufacturer.. Production of PCB ink has reached the world level, in accordance with the requirements of RoHS environmental directives, with excellent quality and high quality service won the trust of the vast number of users, including apple iPhone5 mobile phone manufacturers Foxconn recognition.Company honor and patents
ที่อยู่:
No. 18, Huacheng Road, Industrial Concentration Zone, Qingyang Town, Jiangyin City, Wuxi, Jiangsu, China
ประเภทของธุรกิจ:
ผู้ผลิต/โรงงานผลิต
ขอบเขตธุรกิจ:
กระเป๋า เคส และกล่อง, บรรจุภัณฑ์และการพิมพ์, ผลิตภัณฑ์คอมพิวเตอร์, อุตสาหกรรมเบาและของใช้ประจำวัน, เคมีภัณฑ์, เครื่องจักรการผลิตและแปรรูป, เครื่องมือและเครื่องวัด, ไฟฟ้าและอุปกรณ์อิเล็กทรอนิกส์, ไฟและแสงสว่าง
แนะนำบริษัท:
Jiangsu KASSHUN PHSENSIVitIVITY NEW PRODUCTION CO., Ltd...Committed พัฒนาและผลิตวัสดุที่มีความไวต่อแสงสูงและใช้เทคโนโลยีชั้นสูงส่วนใหญ่จะผลิตขึ้นในด้าน R & D และจำหน่ายหมึก PCB บริษัทมีประสิทธิภาพการทำงานสูงจากผู้ผลิตหมึก PCB ภายใน ... การผลิตหมึก PCB ได้ก้าวขึ้นสู่ระดับโลกตามข้อกำหนด RoHS ด้วยคุณภาพที่ยอดเยี่ยมและบริการคุณภาพสูงทำให้ได้รับความไว้วางใจจากผู้ใช้จำนวนมากรวมถึงผู้ผลิตโทรศัพท์มือถือ Apple iPhone5 Foxconn Recognition
มณฑลเจียงซูคุณจีซซูซานผ่านมาตรฐาน ISO9001 และระบบการจัดการสิ่งแวดล้อม ISO 14000 เป็นบริษัทไฮเทคของประเทศ ผลิตภัณฑ์ตะกั่วบัดกรีมาสก์ผงตะกั่วของบริษัทรุ่นหลัก KSM-S6188, KSM-S6189, 180 series ได้รับการรับรองจาก American Security Certification
บริษัทของเรามีความเชี่ยวชาญเฉพาะด้านในผลิตภัณฑ์ประเภทต่างๆ เรายึดมั่นในหลักการของ " คุณภาพมาก่อนการบริการเป็นอันดับแรกการปรับปรุงอย่างต่อเนื่องและนวัตกรรมที่จะตอบสนองความต้องการของลูกค้า " ในการบริหารจัดการและ " ข้อบกพร่องเป็นศูนย์ข้อร้องเรียน " ในฐานะที่เป็นเป้าหมายของคุณภาพ เพื่อเป็นการสร้างความสมบูรณ์แบบให้กับบริการของเราเราจึงผลิตสินค้าที่มีคุณภาพในราคาที่เหมาะสม